Nano-silica in Holcim general use cement mortars: A comparative study with traditional and prefabricated mortars
ISSN
22875301
Date Issued
2024
Author(s)
Mohammadfarid Alvansazyazdi
Jorge Figueroa
Alex Paucar
Gilson Robles
Pablo M. Bonilla-Valladares
Alexis Debut
Mahdi Feizbahr
Abstract
Nano-silica’s growing use in construction, known for enhancing strength and durability by reducing porosity, drives this research’s significance, especially considering Ecuador’s reliance on cement in construction. A comprehensive comparative study on mortars made with General Use cement and aggregates from Pifo and San Antonio quarries has been studied.
It explores the impact of incorporating nano-silica in varying proportions (0.75%, 1.00%, 1.25%) on mortar properties, contrasting them with conventional and prefabricated mortars. laboratory Testing is conducted according to standards to assess both fresh and hardened state properties, and microscopic analysis reveals the optimal nano-silica proportion’s effects on mortar characteristics. Results shows that Incorporating 0.75% nano-silica resulted in a 61% increase in compressive strength at 7 days and.
For a nanosilica content of 1.25%, a 14% increase in compressive strength was observed at 28 days in relation to the conventional mortar and the permeability of the mortar decreased by 30% when adding 0.75% nanosilica. It discusses economic viability and provides insights through SEM and EDS analyses. Overall, it underscores nano-silica’s potential to enhance mortar properties and its relevance in creating more efficient and durable construction materials.
It explores the impact of incorporating nano-silica in varying proportions (0.75%, 1.00%, 1.25%) on mortar properties, contrasting them with conventional and prefabricated mortars. laboratory Testing is conducted according to standards to assess both fresh and hardened state properties, and microscopic analysis reveals the optimal nano-silica proportion’s effects on mortar characteristics. Results shows that Incorporating 0.75% nano-silica resulted in a 61% increase in compressive strength at 7 days and.
For a nanosilica content of 1.25%, a 14% increase in compressive strength was observed at 28 days in relation to the conventional mortar and the permeability of the mortar decreased by 30% when adding 0.75% nanosilica. It discusses economic viability and provides insights through SEM and EDS analyses. Overall, it underscores nano-silica’s potential to enhance mortar properties and its relevance in creating more efficient and durable construction materials.